Preparation of Polypropylene Multifunctional White Masterbatch with Antistatic and Anti-aging Properties

中文

南华大学学报(自然科学版)

1673-0062

2014

3

92-94

10.19431/j.cnki.1673-0062.2014.03.021

中山市产学研基金资助项目（2013C2FC0027）； 湖南省教育厅基金资助项目（13C798）；

本校为第一机构

本文通过单因素实验确定制备抗静电防老化的聚丙烯( PP)多功能白色母粒的优化配方.结果表明：载体树脂为60 kg,色素为12 kg,抗静电剂为10 kg,抗氧剂为10 kg,分散剂为6 kg,增容剂为2 kg是制备100 kg的多功能白色母粒的最佳配比.用该功能母粒制备的聚丙烯板材的表面电阻系数为0.6×109,氙灯老化500 h后色牢度为5级.

In this paper, the optimum ratio of preparing the multifunctional white master-batch with antistatic and anti-aging properties was ascertained by single factor experi-ments. The results show that the best ratio for preparing 100 kg multifunctional white mas-terbatch:carrier resin is 60 kg,colorant is 12 kg,antistatic agent is 10 kg,anti-oxygen is 10 kg,dispersant is 6 kg,compatibilizer is 2 kg. The surface resistance of polypropylene plates made from the multifunctional masterbatch is 0. 6í109 ,and the co...