采用金相分析、拉伸试验、动态机械热分析等方法研究了不同含量zn对Mg一0．6Zr合金力学性能及阻尼性能的影响．结果表明，加入微量zn后，Mg一0．6Zr合金的强度和伸长率都得到提高，且强度随zn含量的增加而增大，而伸长率而随zn含量的增加变化不大；阻尼性能有所降低，且随zn含量的增加而降低，这是由晶粒细化和溶质原子增多所导致的结果．

The influence of Zn content on mechanical properties and damping capacities of Mg- 0.6Zr alloy was investigated by using optical microscope, tensile test and dynamic mechanical analysis. The results showed that the tensile strength and elongation of the Mg - 0.6Zr alloy were enhanced by adding trace Zn and the strength increased as the content of Zn while the elongation changed little as the content of Zn increased;meanwhile the damping capacity reduced obviously as the content of Zn increased. The results...