利用激光原位反应技术在TC4钛合金表面制备了无裂纹、组织均匀致密的TiN涂层,并分析了激光氮化层的显微组织、成分和物相,测试了涂层横截面显微硬度、涂层耐磨性能及抗SiO2颗粒高速冲蚀的能力。结果表明:在适当的激光参数下制备的氮化钛涂层与TC4基体之间呈现良好的冶金结合,其界面结合强度为240～270MPa;涂层主要为硬质TiN相,涂层硬度高达1550HV0.1,约为基材的4.5倍;涂层磨损失重量是TC4钛合金的14.7%;在60o冲蚀角度下,基材的冲蚀质量损失为涂层的2倍。

TiN coatings with no crack and uniform compact structure were fabricated on the TC4 titanium alloy by laser micro-fusion in-situ synthesized technology.The micro-structure,chemical composition and phase of the coating were analyzed,in addition,the micro hardness of the coating,bond strength between coating and titanium alloy matrix,and the wear resistance of coating were tested.The resistance of erosion of SiO2 particles with high-speed was also tested.It was found that the bonding strength of TiN coating and TC4 titanium alloy was 240–270MPa ...