为优化TiAlN涂层的沉积参数,采用多弧离子镀技术在不同弧电流条件下于锆合金表面制备TiAlN涂层。利用扫描电子显微镜、能量色散X射线谱、高温热处理炉、划痕仪和X射线衍射仪分析弧电流对TiAlN涂层表面形貌、元素成分、高温抗氧化性、膜基结合力及物相结构的影响。结果表明:随着弧电流的升高,TiAlN涂层表面大颗粒数目逐渐增多,但涂层变得更加致密、孔隙率逐渐降低;弧电流为70 A时所制备的涂层高温抗氧化性能最好;膜基结合力随着弧电流的增加呈现出先增大后减小的趋势,弧电流为60 A时所制备的涂层膜基结合力最大,为32 N;弧电流为50 A时,涂层中物相Ti_3AlN在(111)晶面、物相AlN在(100)晶面表现出择...

TiA1N coatings were deposited on the surface of zirconium alloys by multi-arc ion plating with different arc currents. The effect of arc current on surface morphology, elemental composition, high temperature oxidation resistance, adhesion strength and phase structures of TiAlN coatings was analyzed by scanning electron microscopy （SEM）, energy dispersive spectroscopy （EDS）, high temperature heat treatment furnace, scratch tester and X-ray diffractometer（ XRD）, respectively. Results showed that the quantity of large particles on TiA1N coat...